Descriptions
Specifications:
Thickness: 0.05-2mm (can be customized)
Width: 10-1500mm (can be customized)
Color: transparent, foggy (any colors can be customized)
Advantages
Great hydrolysis resistance: polyether TPU film has better hydrolysis resistance and will not occur significant hydrolysis when placed in water at room temperature for 1-2 years.
Yellowing resistance: due to the raw material's resistance to yellowing, the yellowing resistance of polyether TPU film can generally reach above grade 4.
Low temperature resistance: polyether TPU film can still keep good elasticity and softness at - 40 degrees without embrittlement and vitrification.
Good anti-mold and anti-bacterial properties: polyether TPU film has strong resistance to penicillium, aspergillus, short-stalk mould and mixed spore.
Polyether TPU film is often used in medical products, water life saving products and water sports products.
Applications
Medical, wound dressing, probe cover, blood bag, surgical drapes
Automobile, seat, headrest, air bag
Outdoor sports products, tent, balloon, water bladder, jacket
Home textile, fabric lamination
Architecture, roof, floor
Electron industry
Physical Performance
| TEST ITEM | TEST METHOD | UNIT | TEST VALUE |
|---|---|---|---|
| Hardness | ISO 686 | shoreA | 90±2 |
| Specific Gravity | ISO 2781 | g/cm3 | 1.14±0.02 |
|
Thickness Color |
Thickness Gauge Visual Inspection |
mm / |
0.05-2.0 Customized |
| Tensile Strength | ISO 527-3/5/500 | MPa |
CD: 39.1 MD: 36.3 |
| Tensile Strength @ 50% Elongation | ISO 527-3/5/500 | MPa |
CD: 8.29 MD: 8.19 |
| Tensile Strength @ Elongation | ISO 527-3/5/500 | MPa |
CD: 11.07 MD:10.93 |
| Tensile Strength @ 300% Elongation | ISO 527-3/5/500 | MPa |
CD: 15.78 MD: 14.54 |
| Elongation at Break | ISO 527-3/5/500 | % |
CD: 836 MD: 792 |
| Tear Strength | ISO 34-1B | kN/m |
CD: 118.4 MD: 110.0 |
| Abrasion Resistance | ISO 4649 | mm3 | 36 |
| Vicat Softening Point A50 | ISO 306 | ℃ | 97℃ |
| Melting Point | Kofler | ℃ | 165-175 |
| Brittle Point | DSC | ℃ | -50℃ |